TiO2-N memungkinkan pemanfaatan sinar matahari sebagai sumber energi dalam membentuk •OH yang berperan sebagai oksidator untuk mendegradasi fenol pada limbah cair industri batik. TiO2-N dibuat dengan berbagai variasi perbandingan mol TiO2:urea yaitu 75:25; 50:50; 25:75 dan 10:90. Proses fotodegradasi dilakukan penentuan kondisi terbaik yang meliputi variasi perbandingan TiO2-Urea, variasi waktu kontak, dan variasi pH limbah. Fotokatalis dikarakterisasi menggunakan DRS, SEM, dan FTIR. Hasil penelitian menunjukkan besar energi celah pita untuk fotokatalis TiO2 dan TiO2-N (75:25, 50:50, 25:75, dan 10:90) yaitu 3,2523 eV; 3,2438 eV; 3,2396 eV; 3,2269 eV dan 3,2353 eV. Hasil analisis FTIR menunjukkan adanya pergeseran intensitas serapan O-Ti-O yaitu pada TiO2 (532 cm-1 dan 686 cm-1) dan TiO2-N (524 cm-1dan 678 cm-1) yang mengindikasikan telah terbentuk ikatan Ti-N. Analisis SEM menunjukkan TiO2 dan TiO2-N berbentuk granular dan tidak homogen, Perbedaan kenampakkan fisik yaitu partikel TiO2-N berbentuk aglomerasi. Aktivitas fotokatalis TiO2-N terbesar pada TiO2-N (25:75) dengan persentase degradasi 35,82%. Waktu kontak optimum pada perbandingan TiO2-urea optimum untuk degradasi fenol adalah 6 jam dengan persentase degradasi 48,59%. pH optimum degradasi fenol adalah pH basa yaitu pH 13 dengan persentase degradasi 74,67%. Hal ini menunjukkan bahwa fenol dapat didegradasi dari limbah cair batik dan metode fotodegradasi dapat diaplikasikan untuk mengatasi limbah cair organik.

Abtrak (Bhs. Inggris)

ABSTRACT
TiO2-N which allows the utilization of sunlight as a source of energy in the form of •OH that acts as an oxidant to degrade phenol in batik industry waste-water has been conducted. TiO2-N was made by various ratio mol of TiO2 : urea of 75:25; 50:50; 25:75 and 10:90. The optimum conditions was determined in the photodegradation process that include variations of TiO2-urea ratio, contact time variations, and pH of waste variations. fotocatalys were characterized using DRS, SEM, and FTIR. The results showed that the band gap energy of the photocatalyst TiO2 and TiO2-N (75:25, 50:50, 25:75, and 10:90) were 3.2523 eV; 3.2438 eV; 3.2396 eV ; 3.2269 eV and 3.2353 eV respectively. FTIR analysis results showed a shift absorption intensity of O-Ti-O is  decreased on TiO2 (532 cm-1 and 686 cm-1) and TiO2-N (524 cm-1 and 678 cm-1) which indicated that is formed were in Ti-N. SEM analysis showed that particles showed both granular form and were not homogeneous. The difference the physical morphology is that the particles of TiO2-N is aglomeration form. The largest activity of TiO2 photocatalyst is TiO2-N (25:75) with the percentage degradation of 35.82%. Optimum contact time on the optimum ratio of TiO2-urea for the phenol degradation was 6 hours with the percentage of degradation up to 48.59%. The optimum pH is at 13 with the percentage of degradation of 74.67%. These result that phenol can be degraded from batik waste-water and the photodegradation method can be applied to overcome the organic liquid waste.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman