Kitosan banyak dimanfaatkan sebagai adsorben pengolahan zat warna. Methyl orange dan malachite green merupakan zat warna yang sering digunakan dalam industri tekstil dan memiliki efek berbahaya. Karboksimetil kitosan telah disintesis dalam penelitian ini untuk diketahui karakteristiknya untuk aplikasinya dalam penurunan kadar zat warna (methyl orange dan malachite green). Sintesis karboksimetil kitosan dilakukan dengan mereaksikan larutan kitosan yang dikondisikan dalam suasana basa menggunakan larutan NaOH 40% dengan asam monokloroasetat dengan perbandingan 1:7 (b/v). Kitosan dan karboksimetil kitosan selanjutnya dilakukan karakterisasi dengan FTIR dan PSA. Kajian adsorpsi karboksimetil kitosan terhadap zat warna dilakukan dengan variasi pH, waktu kontak, dan konsentrasi zat warna. Spektra IR yang dihasilkan menunjukkan terbentuknya karboksimetil kitosan yang ditunjukkan adanya gugus C=O pada bilangan gelombang 1599,06 cm-1 dengan ukuran partikel sebesar 281 nm berdasarkan hasil karakterisasi dengan PSA. Karboksimetil kitosan mampu mengadsorpsi methyl orange secara optimum pada pH 3, waktu kontak 100 menit, dengan kapasitas adsorpsi sebesar 0,52 mg/g mengikuti pola isoterm adsorpsi Freundlich. Sedangkan adsorpsi terhadap malachite green terjadi secara optimum pada pH 5, waktu kontak 100 menit, dengan kapasitas adsorpsi sebesar 0,91 mg/g mengikuti pola isoterm adsorpsi Langmuir.

Abtrak (Bhs. Inggris)

Chitosan was widely used as an adsorbent for dye processing. Methyl orange and malachite green were dyes, they had been using in the textile industry and have harmful effects. Carboxymethyl chitosan was synthesized in this study to determine its characteristics for its application to reducing levels of dyes (methyl orange and malachite green). The synthesis of carboxymethyl chitosan was carried out by reacting the chitosan solution which was conditioned in an alkaline environment using 40% NaOH solution with monochloroacetic acid in the ratio 1:7 (w/v). Chitosan and carboxymethyl chitosan were characterized by FTIR and PSA. The study of carboxymethyl chitosan adsorption on dyes was carried out with pH, contact time, and concentration variations. The resulting IR spectra showed the formation of carboxymethyl chitosan which was indicated by the presence of a C=O groups at wave number 1599.06 cm-1 with 281 nm of particle size based on the results of characterization with PSA. Carboxymethyl chitosan was able to adsorb methyl orange optimally at pH 3, contact time of 100 minutes, with an adsorption capacity of 0.52 mg/g following the Freundlich adsorption isotherm pattern. Meanwhile, the optimum adsorption of malachite green occurred at pH 5, contact time of 100 minutes, with an adsorption capacity of 0.91 mg/g following the Langmuir adsorption isotherm pattern.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman