SINTESIS DAN UJI AKTIVITAS KOMPOSIT TiO2/POLIANILIN TERHADAP PENURUNAN KADAR AMONIA DAN NITRIT PADA LIMBAH CAIR TAHU
Abstrak (Bhs. Indonesia)
Degradasi amonia dan nitrit telah dilakukan dengan menggunakan fotokatalis TiO2/Polianilin yang disintesis menggunakan metode impregnasi langsung. Garam emeraldine dari Polianilin yang dihasilkan berwarna hijau dan komposit TiO2/Polianilin yang dihasilkan berwarna abu-abu. Fotokatalis dikarakterisasi menggunakan SEM (ScanningElectron Microscopy), EDX (Energy Dispersive XRay Spectroscopy), dan XRD (X-Ray Difraction). Penambahan 1%, 5% dan 10% (b/b) polianilin diketahui dapat meningkatkan aktivitas fotokatalitik TiO2. Fotokatalis TiO2/Polianilin 10% terbukti memberikan penurunan degradasi amonia dan nitrit tertinggi yaitu sebesar 37,71% dan 60,67%. Degradasi amonia dan nitrit meningkat menjadi 59,02% dan 72,25% pada suasana asam yaitu pada pH 3 dengan waktu optimum 240 menit dibawah sinar UV. Laju kinetika diperoleh mengikuti orde satu dengan konstanta laju fotodegradasi amonia dan nitrit sebesar 0,003717 menit-1 dan 0,005342 menit-1. Uji penggunaan kembali (reusable) dilakukan sebanyak 4 kali dengan menghasilkan persen degradasi amonia dan nitrit terakhir sebesar 10,90% dan 15,01%, hal ini dapat dikatakan bahwa TiO2/Polianilin memiliki sifat reusable yang kurang baik.
Abtrak (Bhs. Inggris)
Degradation of ammonia and nitrite have been carried out using photocatalyst TiO2/Polyaniline synthesized using a direct impregnation method. The resulting emeraldine salt from Polyanilin is green and the resulting TiO2/Polyaniline composite is gray. the photocatalyst is characterized using SEM (Scanning Electron Microscopy), EDX (Energy Dispersive X-Ray Spectroscopy), and XRD (X-Ray Diffraction). The addition of 1%, 5%, and 10% (w/w) polyaniline is known to increase the photocatalytic activity of TiO2. Photocatalyst TiO2/Polyaniline 10% was shown to provide the highest decrease in ammonia and nitrite degradation of 37.71% and 60.67%. Degradation of ammonia and nitrites increased to 59.02% and 72.25% in the acidic atmosphere at pH 3 with an optimum time of 240 minutes under UV light. The kinetic rate is obtained following order one with ammonia and nitrite photodegradation rate constants of 0.003717 minutes-1 and 0.005342 minutes-1. Reusable tests were conducted 4 times resulting in the last percent degradation of ammonia and nitrites of 10.90% and 15.01%, it can be said that TiO2/Polyaniline has poor reusable properties.
Kata kunci
Pembimbing 1
Pembimbing 2
Pembimbing 3
Tahun
Jumlah Halaman
Save