Material polianilin dalam bentuk garam emeraldin berhasil disintesis dengan menggunakan metode polimerisasi antarmuka. Material polianilin dikompositkan dengan penambahan ZnO sebanyak 0, 1, 5, 10 % (b/b). Polianilin/ZnO nanokomposit terbukti dapat menurunkan konsentrasi congo red lebih baik dibandingkan polianilin. Material dikarakterisasi menggunakan SEM (Scanning Electron Microscopy), EDX (Energy Dispersive XRay Spectroscopy), dan FTIR (Fourier Transform Infra-Red). Material polianilin/ZnO 5% memberikan kondisi optimum dalam menurunkan konsentrasi congo red melalui dua mekanisme  proses, yaitu proses adsorpsi dan fotokatalisis. Pada suasana pH 7 dengan waktu kontak selama 60 menit serta di bawah kondisi penyinaran UV, material polianilin/ZnO 5% memberikan kondisi optimum dalam menurunkan konsentrasi congo red 100 ppm dengan persen penurunan sebesar 94,39%. Laju kinetika penurunan konsentrasi congo red polianilin/ZnO berjalan mengikuti persamaan laju kinetika orde satu dengan konstanta laju fotodegradasi congo red tertinggi ditunjukkan oleh polianilin/ZnO 5% sebesar 0,112929 menit-1. Stabilitas polianilin/ZnO dengan 3 kali pengulangan memberikan persen penurunan konsentrasi congo red 25 ppm sebesar 6%. Regenerasi polianilin/ZnO menggunakan HCl terbukti dapat mengaktifkan kembali polianilin/ZnO dalam menurunkan konsentraasi congo red.

Abtrak (Bhs. Inggris)

Polyaniline material in the form of emeraldin salt was successfully synthesized using the interface polymerization method. Polyaniline material is composited by adding ZnO as much as 0, 1, 5, 10% (w/w). Polyaniline/ZnO nanocomposite has been shown to reduce congo red concentration better than polyaniline. The material is characterized using SEM (Scanning Electron Microscopy), EDX (Energy Dispersive X-Ray Spectroscopy), and FTIR (Fourier Transform Infra-Red). Polyaniline/ZnO 5% provides optimum conditions in reducing the concentration of congo red through two process mechanisms, namely the adsorption process and photocatalysis. At a pH 7 with a contact time of 60 minutes and under UV irradiation conditions, polyaniline/ZnO 5% provides optimum conditions in reducing the concentration of 100 ppm congo red with a percent decrease of 94.39%. The kinetic rate of the decrease in polyaniline/ZnO congo red concentrations proceeded following the first order kinetic equations with the highest congo red photodegradation rate constants shown by polyaniline/ZnO 5% at 0.112929 minutes-1. The stability of polyaniline/ZnO with 3 repetitions gave a 6% decrease in the concentration of congo red 25 ppm. Polyaniline/ZnO regeneration using HCl is proven to be able to reactivate polyaniline/ZnO in reducing congo red concentration.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman