Barium ferit yang di doping  〖"Ni" 〗^"2+"  konsentrasi  0,7 mol dengan variasi temperatur sintering 450ºC (hanya pre-sintering), 600ºC, 700 ºC, dan 800ºC telah dibuat menggunakan metode modified solid state reaction. Sampel dianalisis fasa kristal, ukuran kristal, sifat magnetik dan penyerapan gelombang mikronya. metode modified solid state reaction merupakan perpaduan antara metode sol-gel dan solid state reaction, yang meliputi pembuatan larutan prekusor awal, sol-gel, pemadatan, pre- sintering dan sintering. Sampel yang telah dibuat selanjutnya dikarakterisasi dengan alat X-Ray Diffraction (XRD),Vibrating Sample Magnetometer (VSM) dan Vector Network Analyzer (VNA). Hasil karakterisasi menunjukkan bahwa semua sampel yang telah disintesis mengandung dua fasa yaitu  BaFe2O4  dan Ni〖"Fe" 〗_"2"  "O" _"4" . Kurva histerisis menunjukkan bahwa semua sampel merupakan material superparamagnetik. Material penyerap gelombang mikro yang baik memiliki refleksi hilang yang tinggi dan bandwith yang lebar. Pada temperatur 700ºC menunjukkan hasil terbaik dengan rentang frekuensi penyerapan terbanyak pada frekuensi 8,14 GHz – 8,54 GHz; 9,88 GHz–10,88 GHz; 11,70 GHz – 12,00 GHz dan memiliki penyerapan yang paling tinggi dibandingkan dengan ketiga sampel lainya yakni pada frekuensi 8,30 GHz sebesar  -27,30 dB. Berdasarkan hasil yang diperoleh bahwa variasi temperatur sintering telah berpengaruh pada fasa kristal, ukuran kristal, sifat megnetik, dan penyerapan gelombang mikronya. Dengan demikian Ni- Barium Ferit sangat berpotensi sebagai material absorpsi gelombang mikro.

Abtrak (Bhs. Inggris)

Barium ferrite doped 〖Ni〗^(2+)concentrations of 0,7 mol with sintering temperature variations is 450ºC (pre-sintering only), 600ºC, 700ºC, and 800ºC have been made with modified solid state reaction method. Samples were analyzed crystal phase, crystal size, magnetic properties and microwave absorption. The modified solid state reaction method is a combination of sol-gel and solid state reaction methods, first preparing initial precursor solutions, sol-gel, compaction, pre-sintering and finally sintering. The samples were characterized by X-Ray Diffraction (XRD), Vibrating Sample Magnetometer (VSM) and Vector Network Analyzer (VNA). The characterization results show that all samples that have been synthesized contain two phases namely 〖"BaFe" 〗_"2"  "O" _"4"  and 〖"NiFe" 〗_"2"  "O" _"4" .  The hysteresis curve shows that all samples are superparamagnetic materials. Good microwave absorbent material has a high reflection loss and a wide bandwidth. At 700ºC show the best results with a the greatest number of distance in frequency 8,14 GHz – 8,54 GHz; 9,88 GHz – 10,88 GHz; 11,70 GHz – 12,00 GHz and have a best absorbent than other sample in a frequency 8,30 GHz a number of -27,30 dB. Based on the results obtained that sintering temperature variations have influenced the crystalline phase, crystal size, megnetic properties, and microwave absorption. Thus Ni- Barium Ferrite is highly potential as a microwave absorbent material.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman