Sel surya lapisan tipis ZnO:CNT tersensitasi dye ekstrak daun bayam (Amaranthus Hybridus l) telah difabrikasi sebagai fotosensitizer. Telaah pengujian spektrum FTIR menunjukkan bahwa adanya ikatan gugus fungsi C-H pada rentang 2850-2970cm-1. Hal tersebut menunjukkan adanya pengotor senyawa organik yang tertangkap pada lapisan tipis ZnO:CNT. Pengujian XRD sampel S3 menunjukkan munculnya peak dye pada sudut 28.4o, 30.78o, 32.4o, 42.48o, 50.5o, 60.46 o, sedangkan pada pengujian SEM sampel S3 menunjukkan adanya senyawa bentukan baru antara ZnO:CNT dan dye dengan ketebalan 15.3µm-35.5µm. Dari hasil pengujian listrik diperoleh nilai arus sampel S2=0,8 μA, tegangan sampel S2=289 mV, efisiensi sampel S2=0,0003%, sedangkan arus sampel S3=0,85 μA, tegangan sampel S3=292mV, efisiensi sampel S3=0,0004%. Hal ini menunjukkan bahwa penambahan dye daun bayam dapat meningkatkan nilai arus dan tegangan serta nilai efisiensi pada lapisan tipis ZnO:CNT sehingga dapat digunakan sebagai sensitizer solar cell.

Abtrak (Bhs. Inggris)

Spinach leaves (Amaranthus Hybridus l) extract dye sensitized thin layer ZnO:CNT fabricated as a photosensitizer. The study of testing result FTIR spectrum there is C-H bond functional groups in the range of 2850-2970 cm-1. This indicate organic compound impurities caught on a thin layer of ZnO: CNT. XRD testing of samples S3 shows the emergence of dye peak at an angle of 28.4 o, 30.78 o, 32.4 o, 42.48 o, 50.5 o, 60.46 o, whereas the SEM examination of samples S3 indicates the formation of new compounds between ZnO: CNT and dye thickness 15.3μm -35.5μm. From the test results can be obtained electric current value sample S2 = 0.8 uA, the sample voltage S2 = 289 mV, the efficiency of sample S2 = 0.0003%, while the current sample S3 = 0.85 uA, voltage sample S3 = 292mV, the efficiency of sample S3 = 0.0004%. This is indicating that the addition of spinach leaves dye may increase the value of current and voltage as well as the efficiency of the thin layer of ZnO: CNT so that it can be used as a sensitizer solar cell.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman