Barium hexaferit tersubtitusi ion-ion La3+ disintesis dengan variasi konsentrasi La3+ (0 ≤ x ≤ 0,2) menggunakan metode hibrid sol-gel. Sampel dianalisa fasa kristal, ukuran kristal, sifat magnetik dan penyerapan gelombang mikronya. Proses metode hibrid sol-gel adalah perpaduan antara metode sol-gel dan solid state reaction, meliputi pembuatan larutan bahan awal, sol-gel, pemadatan, dan sintering. Sampel yang telah diperoleh dikarakterisasi dengan x-ray diffraction (XRD), vibrating sample magnetometer (VSM) and vector network analyzer (VNA). Hasil karakterisasi menunjukkan bahwa semua sampel yang telah disintesis merupakan multi fasa. Pada konsentrasi 0,1 mol menunjukkan tiga puncak fasa BaLaFeO4 dengan ukuran kristal terkecil. Kurva histerisis menunjukkan bahwa semua sampel merupakan material superparamagnetik. Pada konsentrasi 0,1 mol diperoleh nilai magnetisasi saturasi (Ms) yang tinggi dan nilai koersivitas yang rendah. Pada konsentrasi 0,1 mol menunjukkan bahwa refleksi maksimum yang hilang -34,15 dB pada 8,4 GHz. Berdasarkan hasil yang diperoleh bahwa variasi konsentrasi La3+ telah berpengaruh pada fasa kristal, ukuran kristal, sifat megnetik, dan penyerapan gelombang mikronya maka barium hexaferit tersubtitusi ion-ion La3+ sangat berpotensi untuk material penyerap gelombang mikro.

Abtrak (Bhs. Inggris)

Barium hexaferrite substituted by La3+ ions were synthesized with the variation of La3+ (0 ≤ x ≤0,2) using hibrid sol-gel method. The crystal phase, crystal size, magnetic properties and microwave absorption of the samples were analyzed. The process of hibrid sol-gel method are synthesis sol-gel and solid state reaction method, include fabricating initial substance solutions, sol-gel, pressing, and sintering. The obtained sample have been characterized by x-ray diffraction (XRD), vibrating sample magnetometer (VSM) and vector network analyzer (VNA). The results of characterization indicate that all the synthesized samples were multi phase. In consentration 0,1 mol showed three peak of BaLaFeO4 phase with smallest crystal size. Hysteresis loops showed that all samples are superparamagnetic materials. In consentration 0,1 mol obtained the highest value of saturation magnetizaton (Ms) and the low coersivity. In consentrastion 0,1 mol showed that the maximum reflection losses -34,15 dB at 8,4 GHz. Based on the obatained results that variation consentration of La3+ have been influential to crystal phase, crystal size, magnetic properties, and the microwave absorption, therefore barium hexaferrites substituted by La3+ ions are potential for microwave absorbing materials.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman