Material stronsium ferit dengan doping lantanum oksida telah dibuat menggunakan metode solid state reaction dengan komposisi (6)Fe2O3:(x)La2O3:(1-x)SrO ,dimana x = 0,2 mol. Metode solid state reaction terdiri dari calcination, mixing, milling variasi waktu t = 0,5; 1,0 dan 1,5; jam, compaction, annealing pada suhu 800 °C selama 1 jam, dan sintering pada suhu 1100 °C selama 3 jam. Karakterisasi XRD, VSM, dan VNA telah dilakukan untuk menganalisis struktur, sifat magnetik, dan penyerapan gelombang mikronya. Hasil karakterisasi menunjukkan fasa-fasa Sr0,5La0,5Fe12O19, SrFe12O19 dan Fe2O3 terbentuk struktur rhombohedral dan hexagonal.  Nilai magnetiasi saturasi (Ms) menurun dan magnetisasi remanen (Mr) menurun dan medan koersivitas (Hc) meningkat. Nilai permeabilitas relatif  (μr) dan suseptibilitas (χm) menurun. Nilai absorpsi gelombang mikro tertinggi yaitu sampel LSFM-2 pada frekuensi 7,69 GHz sebesar 35,99 dB. Secara umum. semakin lama waktu milling maka fasa terbentuk berkurang dan sifat magnetik relatif stabil serta absorbsi gelombang mikro semakin tinggi. Material magnetik ini sangat menjanjikan untuk aplikasi-aplikasi absorpsi elektromagnetik interference (EMI) untuk frekuensi 8 – 12 GHz (X-Band). Secara keseluruhan hasil penelitian ini menunjukan adanya peningkatan performa untuk menyerap gelombang mikro dengan pengaruh waktu milling terhadap pembuatan lantanum stronsium ferit.

Abtrak (Bhs. Inggris)

Doping strontium ferrite material with lanthanum oxide has been made using solid state reaction method with composition (6) Fe2O3 (x) La2O3: (1-x) SrO, where x = 0.2 mol. Solid state reaction method consists of calcination, mixing, milling variation of time t = 0.5; 1.0 and 1.5 hours, compaction, annealing at a temperature of 800 ° C for 1 hour, and sintering at 1100 ° C for 3 hours. Characterization XRD, VSM, and VNA has been done to analyze the structure, magnetic properties, and microwave absorption. The results showed phase Sr0,5La0,5Fe12O19, SrFe12Fe19 and Fe2O3 formed each rhombohedral and hexagonal structure. Meanwhile, the value magnetiasi saturation (Ms) dicreases, remanent magnetization (Mr) dicreases, field coercivity (Hc) increases. Relative permeability (μr) and Susceptibility (χm) dicreases. Value absorption of microwave is available from LSFM-2 samples with longer time of 1 hour at a frequency of 7.69 GHz at 35.99 dB. Generally, longer  milling time phase is reduced and stable magnetic properties as well higher microwave absorption. The magnetic materials is very promising for applications absorption of electromagnetic interference (EMI) to frequency of 8-12 GHz (X-Band). As result research show the existence improvement performa to permeate microwave with  effect of milling time in lanthanum  stronsium ferrite of manufacturing.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman