Kejadian lepasnya braket keramik pada masa perawatan ortodontik dapat menyebabkan distorsi pada basis braket. Distorsi yang berupa hilangnya retensi mekanik pada basis braket dapat menyebabkan penurunan kekuatan perlekatan ulang. Salah satu metode untuk memberi retensi retensi mekanik tambahan pada basis braket keramik adalah sandblasting menggunakan beberapa partikel abrasif. Penelitian ini bertujuan untuk membandingkan kekuatan geser perlekatan ulang braket keramik menggunakan sandblasting aluminium oxide dan silica coating dengan penambahan silane. Penelitian dilakukan secara eksperimental laboratoris dengan rancangan post test only control group desain yang terdiri atas 3 kelompok, yaitu kelompok I (silane), kelompok II (sandblasting aluminium oxide + silane) dan kelompok III (silica coating + silane). Sampel penelitian adalah 21 braket keramik yang dilakukan uji geser dan 2 sampel dari masing-masing kelompok dilakukan uji scanning electron microscopy (SEM). Uji one way ANOVA menunjukkan perbedaan yang signifikan antara ketiga kelompok sampel. Kelompok III memiliki kekuatan geser tertinggi diikuti dengan kelompok II dan kelompok I. Hasil uji SEM pada kelompok III menunjukkan mikroporositas yang teratur dan homogen. Kekuatan geser pada kelompok III lebih tinggi karena adanya proses triboplasma yang menyebabkan mikroretensi yang terbentuk lebih baik dan adanya reaktivitas silane yang berikatan kuat dengan silica. Kekuatan geser tersebut dua kali lebih besar jika dibandingkan dengan kekuatan geser yang optimal untuk perawatan ortodontik. Hal tersebut dapat menyebabkan kecenderungan untuk terjadi fraktur enamel pada saat debonding.

Abtrak (Bhs. Inggris)

The incidence of debonded ceramic bracket in the orthodontic treatment can cause distortion at the bracket base. Distortion due to mechanical retention on the bracket base is lost can reduce bond strength of bracket rebonding. One method to created addition mechanical retention at the bracket base is sandblasting with abrasif sands. The aim of this study was to compare of shear bond strength between rebonded ceramic bracket using aluminium oxide sandblasting and silica coating with addition of silane. This study was an experimental-laboratory study with post test only control group design were randomly divided into 3 groups as follow: Group I (silane), Group II (sandblasting aluminium oxide + silane) and Group III (silica coating + silane). This study was carried on 21 ceramic brackets were done shear strength test, continued by scanning electrone microscopy (SEM) test. Normality and homogenity shows normal distribution of the population. One way ANOVA analysis was used to showed significant differences among the three groups, and the result is p=0,000, continued by Post hoc LSD test. The bond strength of recycled ceramic bracket in group III was higher than group II follow group I. SEM micrographs in group III also showed greater irregularities and homogenity on the surface of the ceramic bracket base. The shear bond strength in group III more high because the process of triboplasma created microretention better and reactivity of silane which bind strongly with silica. That shear strength is twice as high when compared with optimal shear strength for orthodontic treatment. It can lead a tendency to fracture the enamel during debonding.

Kata kunci

Pembimbing 1

Pembimbing 2

Pembimbing 3

Tahun

Jumlah Halaman